Thread locker grades

Grade Colour Viscosity Gap fill Breakaway torque Prevailing torque Service temp Fixure time Full cure Application details
AA 222.0 Purple 900 to 1500 0.2 mm 4 to 8Nm 3 to 6 Nm - 65 to + 300 °F 20 min 24 hr General Purpose , used whereever easy disassembly is required
AA 241.0 Blue 100 to 150 0.1 mm 14 to 20 Nm 10 to 20 Nm -65 to + 300°F 30 min 24 hr Medium Strength, used for small threads Medium Strength, fast curing.
AA 242.0 Blue 900 to 1200 0.2 mm 10 to 20 Nm 4 to   10 Nm - 65 to + 300 °F 15 min. 24 hr. Medium strength, thixotropic with control flow, for regular disassembly
AA 243.0 Blue 1500 to 3000 0.25 mm 23 to 30 Nm 10 to 15 Nm - 65 to + 300 °F 15 min 24 hr. Medium strength, fast curing and
Oil tollerent.
AA 262.0 Red 1200 to 2200 0.25 mm 15 to 22 Nm 20 to 30 Nm - 65 to + 300 °F 10 min 24 hr. High Strength, General purpose,
Oil tolerent, good for all metals
AA 271.0 Red 400 to 600 0.2 mm 20 to 35 Nm 25 to 35 Nm - 65 to + 300 °F 10 min 24 hr. Heavy duty sealing and locking. Fast curing
AA 272.0 Red 6000 to 15000 0.3 mm 18 to 30 Nm 20 to 35 Nm - 65 to + 300 °F 30 min. 24 hr. High temperature resistant, slightly oil
tolerent, good for all metals.
AA 277.0 Red 6000 to 8000 0.3 mm 28 to 35 Nm 28 to 35 Nm - 65 to + 300 °F 30 min. 24 hr. Used in locking for larger bolts and nuts. Thixotropic and high strength.
AA 290.1 Green 20 to 40 - 5 to 20 Nm 20 to 40 Nm - 65 to + 300 °F 30 min. 24 hr. High Srength Wicking grade
ANAEROBIC ADHESIVES

Retainer grades

Grade Colour Viscosity gap fill Shear strength Service temp. Fixure time Full cure Application details
AA 603.0 Green 100 - 150 cp 0.1 mm 3800 psi - 65 to + 300 °F  10 min. 24 hr. High strength Retaining compond with good oil tolerence
AA 638.0 Green 1500 - 2500 cP 0.25 mm 4500 psi - 65 to + 300 °F  5 min. 24 hr. Medium strength, fast curing.
AA 641.0 Yellow 500 -     700 cP 0.12 mm 2100 psi - 65 to + 300 °F  20 min. 24 hr. Retaining compound used in applications where deassembly is needed for service
AA 648.0 Green 400 -     600 cP 0.2 mm 4200 psi - 65 to + 300 °F  5 min. 24 hr. Works well in active and passive sufaces, Excellent strength in cylindrical fitting parts.
AA 660.0 Grey Paste 0.5 mm 3,000 psi - 65 to + 300 °F  5 min 24 hr. Used for repairing machine parts
AA 680.0 Green 800 - 1500 cp 0.25 mm 4100 psi - 65 to + 300 °F  10 min 24 hr. Fast curing, used for close fitting metal parts. Tolerates minor oil contaminations.
ANAEROBIC ADHESIVES

Thread sealant grades

Grade Specific
gravity
Colour Viscosity Gap fill Breakaway
torque
Pressure
resistance
Service
temp
Fixure
time
Full
cure
Application details
AA 542.0 1.10 Brown Low viscous
550 -         750 cP
0.15 mm 20 - 30 Nm ≥ 5,690 psi - 65 to + 300 °F  1  - 3 hr. 24 hr. Fast curing. Max pipe size M25.
AA 540.0 1.10 Blue Paste
15,000 -    25,000 cP
0.30 mm 10 - 20 Nm ≥ 5,690 psi - 65 to + 300 °F  3 - 6 hr. 24 hr. Low strength fast curing
AA 565.0 1.10 White 200,000 - 400,000 cP Needed 5 - 10 mm ≥ 5,690 psi - 65 to + 300 °F  3 - 6 hr. 24 hr. General Purpose thread sealant
AA 567.0 1.10 White 300,000 - 600,000 cP Needed 1.5  -   2 Nm ≥ 5,690 psi - 65 to + 300 °F  1 - 3 hr. 24 hr. Used in pipe fitting with coarse metal threads
AA 572.0 1.10 Off-white Thixotropic paste
60,000 -    90,000 cP
0.30 mm 8  - 20 Nm ≥ 5,690 psi - 65 to + 300 °F  1 - 3 hr. 24 hr. Fast curing. Max pipe size M63.
AA 577.0 1.10 Yellow Thixotropic paste
20,000 -    50,000 cP
0.50 mm 20 - 30 Nm ≥ 5,690 psi - 65 to + 300 °F  1 - 3 hr. 24 hr. Fast curing. Max pipe size M75.
ANAEROBIC ADHESIVES

Gasketing compounds

Grade Colour Viscosity Gap fill Pressure
resistance
Service temp. Fixure
time
Full
cure
Application details
AA 573.0 Fluorescent
green
Thixotropic paste
17,000 -   50,000 cP
0.30 mm ≥ 1,750 psi - 65 to + 300 °F  1 - 3 hr. 24 hr. Medium strength, fast curing.
AA 574.0 Red Thixotropic paste
30,000 - 100,000 cP
0.50 mm ≥ 1,750 psi - 65 to + 300 °F  1 - 3 hr. 24 hr. Medium strength, fast curing.
AA 518.0 Red Thixotropic paste
200,000 - 800,000 cP
0.30 mm ≥ 1,750 psi - 65 to + 300 °F  1 - 3 hr. 24 hr. Medium strength, flexible,
fast curing.
AA 510.0 Fluorescent
orange
Thixotropic paste
30,000 -    80,000 cP
0.50 mm ≥ 1,750 psi - 65 to + 300 °F  1 - 3 hr. 24 hr. Medium strength.
AA 515.0 Purple Thixotropic paste
150,000 - 375,000 cP
400 psi - 65 to + 300 °F  1 - 3 hr. 24 hr. Flexible sealant for rigid
machined flanges